BOPI (similar to Kapton® HN)

Kapton® HN BOPI

Properties

BOPI (Biaxial Oriented Polyimide film, similar to Kapton® HN) is achieved by polycondensation of PMDA and ODA in strong polar solvents, through the process of film forming, and then being stretched and Oriented by biax during the course of imine at high temperature. BOPI film (similar to Kapton® HN) is a special kind of polyimide film. Because of biaxial orientation process, BOPI film possesses higher physical, chemical, and electrical properties. It performs successfully in low & high temperature as range of temperature from -452F(-269c) to +500F(+260c) and can be exposed at +752F(400c) in short time. It is widely used as insulation material in F~H class electric motors, electric locomotive, high temperature cables, backing or cover film of FPCB (flexible printed circuit) applications, aerospace industries and so on.

Data Form

Item Properties Unit Values
μm 12.5 25 30 40 50 75
1 Density g/cm3   1.42±0.02
2 Tensile Strength MD ≥ MPa 160 185 175 160 155 150
TD ≥ 155 170 160 150 140 135
3 Elongation at rapture ≥ % 60
4 Shrinkage (only for reference) 150℃ 30min ≤ % 0.15
400℃ 30min ≤ 2.0
5 Breakdown Strength
(48~62Hz)
Average MV/m 210 210 190 170 160 150
Individual 190 190 180 160 135 120
6 *Surface Resistance 200℃ Ω ≥1.0×1013
7 *Volume Resistance 200℃ Ω·m ≥1.0×1010
8 *Dielectric Constant (48~62Hz) --- 3.5
9 *Loss Tangent (48~62Hz) --- ≤0.004
The items marked * are the inherent properties of Polyimide Film, which are not showed on the testing report for outgoing factory.

Specification

  • 1. Width: 1000mm,or Slit into your request width of kapton tape; Thickness tolerance: +-10%
  • 2. Min Qty: 200kgs each size in a lot. Packing: 25--50 Kgs/carton.
Note:The values noted in above technical specification are given only for our customers' reference and should not be used in writing specifications.